Standard | Fe, % | Si, % | Mn, % | Cr, % | Ti, % | Cu, % | Ni, % | P, % | C, % | S, % |
---|---|---|---|---|---|---|---|---|---|---|
Standard | Fe, % | Si, % | Mn, % | Cr, % | Ti, % | Cu, % | Ni, % | P, % | C, % | S, % |
OST 26-291-94 | 96.565–98.1 | < 0.3 | 0.4–0.7 | < 0.25 | < 0.1 | < 0.025 | 1.5–1.9 | < 0.03 | < 0.1 | < 0.03 |
Property |
---|
Property |
According to TU 14-1-2219-77 Note Failed state |
First quality category Note Mechanical properties are not standardized |
Highest quality category Diameter: 3 mm; Temporary resistance: 736 - 981 MPa |
Diameter: 4 mm; Temporary resistance: 589 - 834 MPa |
Diameter: 5mm; Temporary resistance: 539 - 785 MPa |
Diameter: 5mm; Temporary resistance: 539 - 785 MPa |
Standard | Description |
---|---|
Standard | Description |
OST 26-291-94 | |
TU 14-1-2219-77 |