TsA4M1v (TsAM4-1v)
Hardness TsA4M1v, casting under pressure (GOST 25140−93): HB 10 -1 = 65 MPa.
die-casting non-critical parts in various industries.
Classification
| Country | Section | Category |
|---|---|---|
| CIS, Russia, Ukraine | Metals and alloys | Zinc Foundry Alloys |
Chemical composition
| Standard | Fe, % | Si, % | Sn, % | Mg, % | Cu, % | Zn, % | Al, % | Pb, % | Cd, % |
|---|---|---|---|---|---|---|---|---|---|
| GOST 25140-93 | < 0.12 | < 0.03 | < 0.005 | 0.02–0.1 | 0.6–1.3 | 93.925–95.88 | 3.5–4.5 | < 0.02 | < 0.015 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling | Standard | Size, mm | Tension | Classifiers | $$\sigma _{U}$$, $$MPa$$ | $$\epsilon_L$$, % | Treatment |
|---|---|---|---|---|---|---|---|
| Casting | GOST 25140-93 | under pressure | 196 | 0.5 |
Brinell hardness number
| Rolling | Standard | Classifiers | Value, HBW |
|---|---|---|---|
| Casting | GOST 25140-93 | under pressure | 650 |
Standards
| Standard | Description |
|---|---|
| GOST 25140-93 |
Description of chemical elements
| Element | Units of measurement | Description |
|---|---|---|
| Fe | % | Iron |
| Si | % | Silicon |
| Sn | % | Tin |
| Mg | % | Magnesium |
| Cu | % | Copper |
| Zn | % | Zinc |
| Al | % | Aluminium |
| Pb | % | Lead |
| Cd | % | Cadmium |
Description of mechanical properties
| Parameter | Units of measurement | Description |
|---|---|---|
| $$\sigma _{U}$$ | $$MPa$$ | Ultimate tensile strength |
| $$\epsilon_L$$ | % | Elongation at break (longitudinal) |