TSA8M1 (TsAM8-1)

The alloy has good fluidity, good corrosion resistance, high strength characteristics. Melting point: 375 — 404 ° C. Hardness TsA8M1, cast in chill mold (GOST 25140−93) HB 10 -1 = 70 MPa. Hardness TsA8M1, casting under pressure (GOST 25140−93) HB 10 -1 = 90 MPa.

to cast parts in the automotive, tractor, electrical and other industries.

Classification

Country Section Category
CIS, Russia, Ukraine Metals and alloys Zinc Foundry Alloys

Chemical composition

Standard Fe, % Si, % Sn, % Mg, % Cu, % Zn, % Al, % Pb, % Cd, %
GOST 25140-93 < 0.1 < 0.015 < 0.002 0.01–0.06 0.7–1.4 89.51–92.19 7.1–8.9 < 0.01 < 0.006

Information on suppliers

Physical characteristics

Temperature, °C $$\rho$$, $$\frac{kg}{m^3}$$
20 6300

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\epsilon_L$$, % Treatment
Casting GOST 25140-93 in chill mold 235 1.5
Casting GOST 25140-93 under pressure 270 1.5

Brinell hardness number

Rolling Standard Classifiers Value, HBW
Casting GOST 25140-93 in chill mold 700
Casting GOST 25140-93 under pressure 900

Casting and technological parameters

melting point, °C
375–404

Standards

Standard Description
GOST 25140-93

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Sn % Tin
Mg % Magnesium
Cu % Copper
Zn % Zinc
Al % Aluminium
Pb % Lead
Cd % Cadmium

Description of physical characteristics

Parameter Units of measurement Description
$$\rho$$ $$\frac{kg}{m^3}$$ The density of the material

Description of mechanical properties

Parameter Units of measurement Description
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength
$$\epsilon_L$$ % Elongation at break (longitudinal)

Description of the casting and technological parameters

Parameter Units of measurement Description
melting point °C The temperature at which solid crystalline body makes the transition to the liquid state and Vice versa