U8GA

Hardness У8ГА after annealing (GOST 1435−99): HB 10 ^-1 = 187 MPa .

for the production of spring ribbon

Classification

Country	Section	Category
Country	Section	Category
CIS, Russia, Ukraine	Tool steel	Carbon Tool Steel

Chemical composition

Standard	Fe, %	Si, %	Mn, %	Cr, %	Cu, %	Ni, %	P, %	C, %	S, %
Standard	Fe, %	Si, %	Mn, %	Cr, %	Cu, %	Ni, %	P, %	C, %	S, %
GOST 1435-99	97.447–98.7	0.17–0.33	0.33–0.58	< 0.2	< 0.25	< 0.25	< 0.025	0.8–0.9	< 0.018

Information on suppliers

Wish to advertise here?

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\epsilon_L$ , %	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\epsilon_L$ , %	Treatment
Tape	GOST 2283-79			annealing	740	10
Tape	GOST 2283-79			cold-work	740–1180

Brinell hardness number

Rolling	Standard	Classifiers	Value, HBW
Rolling	Standard	Classifiers	Value, HBW
Alloy	GOST 1435-99	annealing	1870

Analogues

Germany
Germany
1.1830 (C85W)

Standards

Standard	Description
Standard	Description
GOST 1435-99

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Mn	%	Manganese
Cr	%	Chrome
Cu	%	Copper
Ni	%	Nickel
P	%	Phosphorus
C	%	Carbon
S	%	Sulfur

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\epsilon_L$	%	Elongation at break (longitudinal)