VZHL8
Production of ingots and cast rods intended for further refining in the production of shaped castings
Production of ingots and cast rods intended for further refining in the production of shaped castings
| Standard | Fe, % | Si, % | B, % | Mn, % | Cr, % | Ti, % | Ni, % | Al, % | Ce, % | P, % | C, % | S, % | Mo, % |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Standard | Fe, % | Si, % | B, % | Mn, % | Cr, % | Ti, % | Ni, % | Al, % | Ce, % | P, % | C, % | S, % | Mo, % |
| OST 1-90127 - 85 | 8–12 | < 0.6 | < 0.06 | < 0.6 | 14–17 | 1.8–2.5 | 57.495–69.1 | 2.5–3.5 | < 0.01 | < 0.02 | 0.1–0.2 | < 0.015 | 4.5–6 |
| Standard | Treatment | Температура испытаний, ° С | Постоянно приложенное напряжение, МПа | Время до разрушения в часах, ч |
|---|---|---|---|---|
| Standard | Treatment | Температура испытаний, ° С | Постоянно приложенное напряжение, МПа | Время до разрушения в часах, ч |
| OST 1-90127 - 85 | Heating to a temperature of 1150 ± 10 ° С, holding 4 hours, air cooling | 800 | 330 | 50 |
| Standard | Description |
|---|---|
| Standard | Description |
| OST 1-90127 - 85 |