VSt3Gps (St3Gps)

shaped and flat products with a thickness of 10 to 36 mm for load-bearing elements of welded structures operating at variable loads at temperatures from -40 to +425 ° C, and for the non-structural elements of welded structures operating at temperatures from -40 to +425 ° C with guaranteed weldability.

Classification

Country	Section	Category
Country	Section	Category
CIS, Russia, Ukraine	Structural steel	Carbonaceous structural steel of ordinary quality

Chemical composition

Standard	Fe, %	Si, %	Mn, %	Cr, %	Cu, %	Ni, %	As, %	P, %	C, %	S, %
Standard	Fe, %	Si, %	Mn, %	Cr, %	Cu, %	Ni, %	As, %	P, %	C, %	S, %
GOST 380-2005	97.46–99.06	< 0.15	0.8–1.1	< 0.3	< 0.3	< 0.3	< 0.08	< 0.04	0.14–0.22	< 0.05

Information on suppliers

Wish to advertise here?

Physical characteristics

Temperature, °C	$\rho$ , $\frac{kg}{m^3}$
Temperature, °C	$\rho$ , $\frac{kg}{m^3}$
20	7850

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{P}$ , $MPa$	$\epsilon_L$ , %	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{P}$ , $MPa$	$\epsilon_L$ , %	Treatment
Steel is hot rolled.		< 20			370–490	245	26	delivery condition

Technological Properties

Weldability	Flake Susceptibility	Propensity to temper brittleness
Weldability	Flake Susceptibility	Propensity to temper brittleness
no limits	not sensitive	not inclined

Standards

Standard	Description
Standard	Description
GOST 380-2005

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Mn	%	Manganese
Cr	%	Chrome
Cu	%	Copper
Ni	%	Nickel
As	%	Arsenic
P	%	Phosphorus
C	%	Carbon
S	%	Sulfur

Description of physical characteristics

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\rho$	$\frac{kg}{m^3}$	The density of the material

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\sigma_{P}$	$MPa$	Proportionality limit
$\epsilon_L$	%	Elongation at break (longitudinal)

Designation of types of weldability

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
no limits		Welding is performed without heating and without subsequent heat treatment
Boundedly welded		Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld		For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures