ZI130
Bars and rods of stainless steel grade 03Х24Н6АМ3 (ЗИ130)
Classification
Chemical composition
Note: Al + Ti < 0.1%
Bars and rods of stainless steel grade 03Х24Н6АМ3 (ЗИ130)
| Standard | Fe, % | Si, % | Mn, % | Cr, % | Cu, % | Ni, % | Zr, % | Ce, % | P, % | C, % | S, % | Mo, % | N, % | ET, % |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| TU 14-1-3880-84 | 61.065–67.15 | < 0.4 | 1–2 | 23.5–25 | < 0.3 | 5.8–6.8 | < 0.1 | < 0.1 | < 0.035 | < 0.03 | < 0.02 | 2.5–3.5 | 0.05–0.15 | < 0.5 |
Note: Al + Ti < 0.1%
| Property |
|---|
| According to TU 14-1-3880-84 Note Quenching 1060 - 1080 ° С in water |
| According to TU 14-1-3880-84 Note Holiday 350 ° С, 1 h., Air cooling |
| Heat-treated samples Note Quenching 1060 - 1080 ° С in water |
| Diameter: 55 mm; Yield Strength:> 390 MPa |
| Diameter: 55 mm; Temporary resistance:> 690 MPa |
| Diameter: 55 mm; Elongation:> 25% |
| Diameter: 55 mm; Impact strength KCU at 20 ° C:> 58.8 J / cm2 |
| Calculated Properties Density: 7.81 g / cm3 |
| Note Resistant to intergranular corrosion |
| Standard | Description |
|---|---|
| TU 14-1-3880-84 | |
| TU 14-1-3966-85 | |
| TU 14-1-5021-91 | |
| TU 14-3-1398-86 |