1.0319 (L210GA)
Classification
| Country |
Section |
Category |
| Germany |
Non-alloy Steels |
Steels with Average C < 0,12% or Rm < 400 MPa |
Chemical composition
| Standard |
Fe, % |
Si, % |
Mn, % |
Al, % |
P, % |
C, % |
S, % |
|---|
| EN 10208-1 |
98.37–99.985 |
< 0.4 |
< 0.9 |
0.015–0.06 |
< 0.03 |
< 0.21 |
< 0.03 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling |
Standard |
Size, mm |
Tension |
Classifiers |
$$\sigma _{U}$$, $$MPa$$ |
$$\sigma_{0.5}$$, $$MPa$$ |
$$\epsilon_L$$, % |
Treatment |
|---|
|
|
|
|
|
335–475 |
210 |
25 |
|
Properties
| Property |
|---|
| According to EN 10208-1 yield strength: > 210 MPa |
| According to EN 10208-1 tensile strength: 335 - 475 MPa |
| According to EN 10208-1 elongation: > 25 % |
| According to EN 10208-1 Weld SAW, COW the bend Test in cold state: d=2T |
| Weldability In ISO/TR 20172 Group: 1.1 |
| Density: 7.84 g / cm3 |
Analogues
| Germany |
CIS, Russia, Ukraine |
USA |
|---|
| StE 210.7 |
20A |
5L Gr A-25 Class I API 5L:2012 |
Standards
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Si |
% |
Silicon |
| Mn |
% |
Manganese |
| Al |
% |
Aluminium |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
Description of mechanical properties
| Parameter |
Units of measurement |
Description |
| $$\sigma_{0.5}$$ |
$$MPa$$ |
Tensile stress required to produce a total elongation of 0.5% |
| $$\sigma _{U}$$ |
$$MPa$$ |
Ultimate tensile strength |
| $$\epsilon_L$$ |
% |
Elongation at break (longitudinal) |