- Main
- Brand
- Germany
- 1.0000 - 1.0799 (Non-alloy Steels)
- 1.0300 - 1.0399 (Steels with Average C < 0,12% or Rm < 400 MPa)
1.0335 (DD13)
Classification
Chemical composition
Standard | Fe, % | Mn, % | P, % | C, % | S, % |
---|---|---|---|---|---|
EN 10111 | > 99.46 | < 0.4 | < 0.03 | < 0.08 | < 0.03 |
Information on suppliers
Mechanical properties at 20 °C
Properties
Property |
---|
According to EN 10111 Thickness: 1.0 - 1.5 mm ; yield strength: 170 - 330 MPa |
According to EN 10111 Thickness: 1.0 - 1.5 mm ; tensile strength: < 400 MPa |
According to EN 10111 Thickness: 1.0 - 1.5 mm ; elongation: > 27 % |
According to EN 10111 Thickness: 1.5 - 2.0 mm ; yield strength: 170 - 330 MPa |
According to EN 10111 Thickness: 1.5 - 2.0 mm ; tensile strength: < 400 MPa |
According to EN 10111 Thickness: 1.5 - 2.0 mm ; elongation: > 28 % |
According to EN 10111 Thickness: 2 - 3 mm ; yield strength: 170 - 310 MPa |
According to EN 10111 Thickness: 2 - 3mm ; tensile strength: < 400 MPa |
According to EN 10111 Thickness: 2 - 3mm ; tensile strength: > 29 % |
According to EN 10111 Thickness: 3 - 11 mm ; yield strength: 170 - 310 MPa |
According to EN 10111 Thickness: 3 - 11 mm ; tensile strength: < 400 MPa |
According to EN 10111 Thickness: 3 - 11 mm ; elongation: > 33 % |
Density: 7.87 g / cm3 |
Analogues
Germany | CIS, Russia, Ukraine | USA |
---|---|---|
St 1403 | 08kp | SAE 1006 |
Standards
Standard | Description |
---|---|
EN 10111 | |
DIN EN 10111:2008 |
Description of chemical elements
Description of mechanical properties
Parameter | Units of measurement | Description |
---|---|---|
$$\sigma_{Y}$$ | $$MPa$$ | Yield strength |
$$\sigma _{U}$$ | $$MPa$$ | Ultimate tensile strength |
$$\epsilon_{L (L_0 = 80 mm)}$$ | % | Elongation at break (longitudinal) (for L0 = 80 mm) |
$$\epsilon_{L (L_0 = 5.65\sqrt{S_o})}$$ | % | Elongation at break (longitudinal) (for L0 = 5.65√So) |