1.0352 (P245GH)

Classification

Country Section Category
Germany Non-alloy Steels Steels with Average C < 0,12% or Rm < 400 MPa

Chemical composition

Standard Fe, % Si, % Mn, % P, % C, % S, %
EN 10222-2 98.06–99.42 < 0.4 0.5–1.3 < 0.025 0.08–0.2 < 0.015

Information on suppliers

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\sigma_{Y}$$, $$MPa$$ $$\epsilon_L$$, % $$\epsilon_T$$, % $$KV_{L}$$, $$J$$ $$KV_{T}$$, $$J$$ Treatment
410–530 220–245 25 23 32 27

Properties

Property
According to EN 10222-2 note A: 890-930°C, in a furnace
According to EN 10222-2 note N: 890-930°C, air
According to EN 10222-2 note NT or QT: 890-930°C, in air, in oil, in water. Vacation 600-640°C in air, furnace
According to EN 10222-2 the Longitudinal sample Thickness: < 35 mm ; yield strength: > 245 MPa
According to EN 10222-2 the Longitudinal sample Thickness: < 35 mm ; tensile strength: 420 - 530 MPa
According to EN 10222-2 the Longitudinal sample Thickness: < 35 mm ; elongation: > 25 %
According to EN 10222-2 the Longitudinal sample Thickness: < 35 mm ; Work strike KV at 0°C [32°F]: > 32 j
According to EN 10222-2 the Longitudinal samples Thickness: 35 - 160 mm ; yield strength: > 220 MPa
According to EN 10222-2 the Longitudinal samples Thickness: 35 - 160 mm ; yield strength: 420 - 530 MPa
According to EN 10222-2 the Longitudinal samples Thickness: 35 - 160 mm ; elongation: > 25 %
According to EN 10222-2 the Longitudinal samples Thickness: 35 - 160 mm ; Work strike KV at 20°C [68°F]: > 171 j
According to EN 10222-2 the Transverse specimens Thickness: < 35 mm ; yield strength: > 245 MPa
According to EN 10222-2 the Transverse specimens Thickness: < 35 mm ; tensile strength: 420 - 530 MPa
According to EN 10222-2 the Transverse specimens Thickness: < 35 mm ; elongation: > 23 %
According to EN 10222-2 the Transverse specimens Thickness: < 35 mm ; Work strike KV at 0°C [32°F]: > 27 j
According to EN 10222-2 the Transverse specimens Thickness: 35 - 160 mm ; yield strength: > 220 MPa
According to EN 10222-2 the Transverse specimens Thickness: 35 - 160 mm ; yield strength: 420 - 530 MPa
According to EN 10222-2 the Transverse specimens Thickness: 35 - 160 mm ; elongation: > 23 %
According to EN 10222-2 the Transverse specimens Thickness: 35 - 160 mm ; Work strike KV at 0°C [32°F]: > 27 j
According to EN 10222-2 the Test at elevated temperature test Temperature 100°C Thickness: < 50 mm ; yield strength: > 195 MPa
According to EN 10222-2 the Test at elevated temperature test Temperature 100°C Thickness: > 50 mm ; yield strength: > 180 MPa
According to EN 10222-2 the Test at elevated temperature test Temperature 150°C Thickness: < 50 mm ; yield strength: > 185 MPa
According to EN 10222-2 the Test at elevated temperature test Temperature 150°C Thickness: > 50 mm ; yield strength: > 175 MPa
According to EN 10222-2 the Test at elevated temperature test Temperature 200°C Thickness: < 50 mm ; yield strength: > 175 MPa
According to EN 10222-2 the Test at elevated temperature test Temperature 200°C Thickness: > 50 mm ; yield strength: > 165 MPa
According to EN 10222-2 the Test at elevated temperature test Temperature 250°C Thickness: < 50 mm ; yield strength: > 160 MPa
According to EN 10222-2 the Test at elevated temperature test Temperature 250°C Thickness: > 50 mm ; yield strength: > 155 MPa
According to EN 10222-2 the Test at elevated temperature test Temperature 300°C Thickness: < 50 mm ; yield strength: > 145 MPa
According to EN 10222-2 the Test at elevated temperature test Temperature 300°C Thickness: > 50 mm ; yield strength: > 135 MPa
According to EN 10222-2 the Test at elevated temperature test Temperature 350°C Thickness: < 50 mm ; yield strength: > 135 MPa
According to EN 10222-2 the Test at elevated temperature test Temperature 350°C Thickness: > 50 mm ; yield strength: > 130 MPa
According to EN 10222-2 the Test at elevated temperature test Temperature 400°C Thickness: < 50 mm ; yield strength: > 125 MPa
According to EN 10222-2 the Test at elevated temperature test Temperature 400°C Thickness: > 50 mm ; yield strength: > 120 MPa
Weldability In ISO/TR 20172 Group: 1.1
Density: 7.84 g / cm3

Analogues

Germany CIS, Russia, Ukraine USA
1.0352 (P245GH) 20-PV P245GH

Standards

Standard Description
EN 10222-2
DIN EN 10222-2:2000
DIN EN 10222-2:2017
DIN EN 10222-2:2017 + prA1:2019

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
P % Phosphorus
C % Carbon
S % Sulfur

Description of mechanical properties

Parameter Units of measurement Description
$$\sigma_{Y}$$ $$MPa$$ Yield strength
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength
$$\epsilon_L$$ % Elongation at break (longitudinal)
$$\epsilon_T$$ % Elongation at break (transverse)
$$KV_{L}$$ $$J$$ Impact energy (longitudinal)
$$KV_{T}$$ $$J$$ Impact energy (transverse)