1.4606 (X5NiCrTiMoVB25-15-2)
Classification
| Country |
Section |
Category |
| Germany |
Stainless and Heat Resisting Steels |
Chemical Resistant and High Temp Ni Alloys |
Chemical composition
| Standard |
Fe, % |
Si, % |
B, % |
Mn, % |
Cr, % |
Ti, % |
Ni, % |
Al, % |
P, % |
C, % |
S, % |
Mo, % |
|---|
|
49.72–59.099 |
< 1 |
0.001–0.01 |
1–2 |
13–16 |
1.9–2.3 |
24–27 |
< 0.35 |
< 0.025 |
< 0.08 |
< 0.015 |
1–1.5 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling |
Standard |
Size, mm |
Tension |
Classifiers |
$$\sigma _{U}$$, $$MPa$$ |
$$\sigma_{0.2}$$, $$MPa$$ |
$$\epsilon_L$$, % |
$$KV_{L}$$, $$J$$ |
Treatment |
|---|
|
|
|
|
solution annealing |
700 |
250 |
35 |
|
|
|
|
|
|
aging |
880–1150 |
550 |
20 |
|
Heat treatment at 880 ° C |
|
|
|
|
aging |
|
|
|
40 |
|
Brinell hardness number
| Rolling |
Standard |
Classifiers |
Value, HBW |
|
|
solution annealing |
212 |
Analogues
| USA |
CIS, Russia, Ukraine |
|---|
| AL 286 |
X6NiCrTiMoVB25-15-2 |
Standards
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Si |
% |
Silicon |
| B |
% |
Bor |
| Mn |
% |
Manganese |
| Cr |
% |
Chrome |
| Ti |
% |
Titan |
| Ni |
% |
Nickel |
| Al |
% |
Aluminium |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
| Mo |
% |
Molybdenum |
Description of mechanical properties
| Parameter |
Units of measurement |
Description |
| $$\sigma_{0.2}$$ |
$$MPa$$ |
Tensile stress required to produce a total elongation of 0.2% |
| $$\sigma _{U}$$ |
$$MPa$$ |
Ultimate tensile strength |
| $$\epsilon_L$$ |
% |
Elongation at break (longitudinal) |
| $$KV_{L}$$ |
$$J$$ |
Impact energy (longitudinal) |