05kp

Non-critical parts produced by cold pressing and landing.

Classification

Country Section Category
CIS, Russia, Ukraine Structural steel Carbonaceous quality structural steel

Chemical composition

Standard Fe, % Si, % Mn, % Cr, % Cu, % Ni, % As, % P, % C, % S, %
GOST 1050-88 > 98.655 < 0.03 < 0.4 < 0.1 < 0.3 < 0.3 < 0.08 < 0.035 < 0.06 < 0.04

Information on suppliers

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\epsilon_L$$, % Treatment
Sheet hot rolled. 4 255–370 28 delivery condition

Brinell hardness number

Rolling Standard Classifiers Value, HBW
Alloy annealing 1110–1310

Technological Properties

Weldability Flake Susceptibility Propensity to temper brittleness
no limits not sensitive not inclined

Critical point temperatures

Ac1, K Ac3(Acm), K Ar1, K
720 880 700

Analogues

USA Germany
G10060 1.0288 (D5-2)
1.0314 (C2C)

Standards

Standard Description
GOST 1050-88

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
Cr % Chrome
Cu % Copper
Ni % Nickel
As % Arsenic
P % Phosphorus
C % Carbon
S % Sulfur

Description of mechanical properties

Parameter Units of measurement Description
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength
$$\epsilon_L$$ % Elongation at break (longitudinal)

Designation of types of weldability

Parameter Units of measurement Description
no limits Welding is performed without heating and without subsequent heat treatment
Boundedly welded Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures

Description of temperatures of critical points

Parameter Units of measurement Description
Ac1 K
Ac3(Acm) K
Ar1 K