08H18N12T (0X18H12T)
cold-rolled sheet and strip for increased strength of various parts and structures to be welded by spot welding, as well as for the manufacture of pipes and other parts; austenitic steel
cold-rolled sheet and strip for increased strength of various parts and structures to be welded by spot welding, as well as for the manufacture of pipes and other parts; austenitic steel
Standard | Fe, % | Si, % | Mn, % | Cr, % | Ni, % | P, % | C, % | S, % |
---|---|---|---|---|---|---|---|---|
Standard | Fe, % | Si, % | Mn, % | Cr, % | Ni, % | P, % | C, % | S, % |
GOST 5632-72 | 65.065–72 | < 0.8 | < 2 | 17–19 | 11–13 | < 0.035 | < 0.08 | < 0.02 |
Rolling | Standard | Size, mm | Tension | Classifiers | \sigma _{U}, MPa | \sigma_{P}, MPa | \epsilon_L, % | Treatment |
---|---|---|---|---|---|---|---|---|
Rolling | Standard | Size, mm | Tension | Classifiers | \sigma _{U}, MPa | \sigma_{P}, MPa | \epsilon_L, % | Treatment |
Pipes are coldly deformed. | GOST 9941-81 | 549 | 37 | |||||
Pipes are hot deformed. | GOST 9940-81 | 510 | 40 | |||||
The plates | GOST 7350-77 | 510 | 205 | 43 | Hardening of 1030-1080 ° C, air cooling | |||
Sheet | GOST 5582-75 | 510 | 35 | Hardening of 1050-1080 ° C, cooling water |
USA | Germany |
---|---|
USA | Germany |
321 | 1.4541 (X6CrNiTi18-10) |
Standard | Description |
---|---|
Standard | Description |
GOST 5632-72 |