09H14N19V2BR1 (EI726, 1H14N18B2BR1)
Rotors, discs, turbine blades.
rotors, disks, turbine blades with a long service life at a temperature of 650−700 deg .; austenitic steel
Classification
| Country |
Section |
Category |
| CIS, Russia, Ukraine |
Heat resistant steels and alloys |
Heat resistant high alloy steel |
Chemical composition
| Standard |
Fe, % |
Si, % |
B, % |
Mn, % |
Cr, % |
Ni, % |
Ce, % |
P, % |
C, % |
S, % |
Nb, % |
W, % |
|---|
| GOST 5632-72 |
58.08–66.03 |
< 0.6 |
< 0.025 |
< 2 |
13–15 |
18–20 |
< 0.02 |
< 0.035 |
0.07–0.12 |
< 0.02 |
0.9–1.3 |
2–2.8 |
Information on suppliers
Physical characteristics
| Temperature, °C |
$$E\cdot 10^{9}$$, $$MPa$$ |
$$\alpha\cdot 10^{6}$$, $$K^{-1}$$ |
$$\varkappa$$, $$\frac{W}{m\cdot K}$$ |
$$\rho$$, $$\frac{kg}{m^3}$$ |
|---|
| 20 |
202 |
|
15.4 |
8120 |
| 100 |
199 |
15.2 |
16.3 |
|
| 200 |
193 |
16.3 |
16.3 |
|
| 300 |
186 |
16.9 |
18 |
|
| 400 |
178 |
17.5 |
19.2 |
|
| 500 |
169 |
17.8 |
21.3 |
|
| 600 |
160 |
18.1 |
23.4 |
|
| 700 |
152 |
18.6 |
25.1 |
|
| 750 |
148 |
|
|
|
| 800 |
|
18.6 |
27.6 |
|
Mechanical properties at 20 °C
| Rolling |
Standard |
Size, mm |
Tension |
Classifiers |
$$\sigma _{U}$$, $$MPa$$ |
$$\sigma_{P}$$, $$MPa$$ |
$$\epsilon_L$$, % |
$$\psi$$, % |
Treatment |
|---|
| Rod |
GOST 5949-75 |
60 |
|
|
510 |
215 |
30 |
44 |
Hardening and tempering |
Technological Properties
| Weldability |
|---|
| Difficult to weld |
Standards
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Si |
% |
Silicon |
| B |
% |
Bor |
| Mn |
% |
Manganese |
| Cr |
% |
Chrome |
| Ni |
% |
Nickel |
| Ce |
% |
Cerium |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
| Nb |
% |
Niobium |
| W |
% |
Tungsten |
Description of physical characteristics
| Parameter |
Units of measurement |
Description |
| $$E\cdot 10^{9}$$ |
$$MPa$$ |
Elastic modulus |
| $$\alpha\cdot 10^{6}$$ |
$$K^{-1}$$ |
Coefficient of thermal (linear) expansion (range 20°C–T) |
| $$\varkappa$$ |
$$\frac{W}{m\cdot K}$$ |
Coefficient of thermal conductivity (the heat capacity of the material) |
| $$\rho$$ |
$$\frac{kg}{m^3}$$ |
The density of the material |
Description of mechanical properties
| Parameter |
Units of measurement |
Description |
| $$\sigma _{U}$$ |
$$MPa$$ |
Ultimate tensile strength |
| $$\sigma_{P}$$ |
$$MPa$$ |
Proportionality limit |
| $$\epsilon_L$$ |
% |
Elongation at break (longitudinal) |
| $$\psi$$ |
% |
Reduction in cross section on fracture |
Designation of types of weldability
| Parameter |
Units of measurement |
Description |
| no limits |
|
Welding is performed without heating and without subsequent heat treatment |
| Boundedly welded |
|
Welding is possible with heating up to 100–120 °C and subsequent heat treatment |
| Difficult to weld |
|
For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing |
| Not applicable for welded structures |
|
|