15H5 (X5)

Pipes, pump components, blades of turbomachines, boilers suspension;

Classification

Country	Section	Category
Country	Section	Category
CIS, Russia, Ukraine	Heat resistant steels and alloys	Heat resistant low alloy steel

Chemical composition

Standard	Fe, %	Si, %	Mn, %	Cr, %	Ni, %	P, %	C, %	S, %
Standard	Fe, %	Si, %	Mn, %	Cr, %	Ni, %	P, %	C, %	S, %
GOST 20072-74	92.195–95.5	< 0.5	< 0.5	4.5–6	< 0.6	< 0.03	< 0.15	< 0.025

Information on suppliers

Wish to advertise here?

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{P}$ , $MPa$	$\epsilon_L$ , %	$\psi$ , %	$KCU\cdot 10^{3}$ , $\frac{J}{m^2}$	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{P}$ , $MPa$	$\epsilon_L$ , %	$\psi$ , %	$KCU\cdot 10^{3}$ , $\frac{J}{m^2}$	Treatment
Pipes are hot deformed.	GOST 550-75				392	216	24	50	980
Rod	GOST 20072-74				390	165	24	50	980	Annealing 840-860 ° C, the furnace

Brinell hardness number

Rolling	Standard	Classifiers	Value, HBW
Rolling	Standard	Classifiers	Value, HBW
Alloy	GOST 20072-74	annealing, hot rolling	217
Pipes are hot deformed.	GOST 550-75		1700

Standards

Standard	Description
Standard	Description
GOST 20072-74

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Mn	%	Manganese
Cr	%	Chrome
Ni	%	Nickel
P	%	Phosphorus
C	%	Carbon
S	%	Sulfur

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\sigma_{P}$	$MPa$	Proportionality limit
$\epsilon_L$	%	Elongation at break (longitudinal)
$\psi$	%	Reduction in cross section on fracture
$KCU\cdot 10^{3}$	$\frac{J}{m^2}$	Impact toughness