15H5VF (H5VF)
Shells and internal components aids refineries and cracking pipes, pump components and other parts, long operating at temperatures up to 600 ° C.
Classification
| Country | Section | Category |
|---|---|---|
| CIS, Russia, Ukraine | Heat resistant steels and alloys | Heat resistant low alloy steel |
Chemical composition
| Standard | Fe, % | Si, % | Mn, % | Cr, % | Ni, % | V, % | P, % | C, % | S, % | W, % |
|---|---|---|---|---|---|---|---|---|---|---|
| GOST 20072-74 | 90.795–94.4 | 0.3–0.6 | < 0.5 | 4.5–6 | < 0.6 | 0.4–0.6 | < 0.03 | < 0.15 | < 0.025 | 0.4–0.7 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling | Standard | Size, mm | Tension | Classifiers | $$\sigma _{U}$$, $$MPa$$ | $$\sigma_{P}$$, $$MPa$$ | $$\epsilon_L$$, % | $$\psi$$, % | $$KCU\cdot 10^{3}$$, $$\frac{J}{m^2}$$ | Treatment |
|---|---|---|---|---|---|---|---|---|---|---|
| Pipes are hot deformed. | GOST 550-75 | 392 | 216 | 22 | 50 | 1180 | ||||
| Rod | GOST 20072-74 | 390 | 215 | 22 | 50 | 1180 | Annealing 840-860 ° C, the furnace |
Brinell hardness number
| Rolling | Standard | Classifiers | Value, HBW |
|---|---|---|---|
| Pipes are hot deformed. | GOST 550-75 | 1700 |
Standards
| Standard | Description |
|---|---|
| GOST 20072-74 |
Description of chemical elements
| Element | Units of measurement | Description |
|---|---|---|
| Fe | % | Iron |
| Si | % | Silicon |
| Mn | % | Manganese |
| Cr | % | Chrome |
| Ni | % | Nickel |
| V | % | Vanadium |
| P | % | Phosphorus |
| C | % | Carbon |
| S | % | Sulfur |
| W | % | Tungsten |
Description of mechanical properties
| Parameter | Units of measurement | Description |
|---|---|---|
| $$\sigma _{U}$$ | $$MPa$$ | Ultimate tensile strength |
| $$\sigma_{P}$$ | $$MPa$$ | Proportionality limit |
| $$\epsilon_L$$ | % | Elongation at break (longitudinal) |
| $$\psi$$ | % | Reduction in cross section on fracture |
| $$KCU\cdot 10^{3}$$ | $$\frac{J}{m^2}$$ | Impact toughness |