36H2N2MFA (36XH1MFA)

For large critical parts discs, mounting screws, etc. D.

Classification

Country Section Category
CIS, Russia, Ukraine Structural steel Alloyed structural steel

Chemical composition

Standard Fe, % Si, % Mn, % Cr, % Cu, % Ni, % V, % P, % C, % S, % Mo, %
GOST 4543-71 94.4–96.25 0.17–0.37 0.25–0.5 1.3–1.7 < 0.3 1.3–1.7 0.1–0.18 < 0.025 0.33–0.4 < 0.025 0.3–0.4

Information on suppliers

Physical characteristics

Temperature, °C $$E\cdot 10^{9}$$, $$MPa$$ $$\alpha\cdot 10^{6}$$, $$K^{-1}$$ $$\varkappa$$, $$\frac{W}{m\cdot K}$$ $$c\cdot 10^{-3}$$, $$\frac{J}{kg\cdot K}$$ $$R\cdot 10^{-6}$$, $$\Omega\cdot m$$
20 212 36 0.278
100 204 12.5 36 0.496 0.335
200 198 12.8 35 0.508 0.432
300 186 13.3 35 0.525 0.517
400 173 13.5 34 0.538 0.613
500 166 14 33 0.567 0.72
600 156 14.3 31 0.601 0.825
700 139 14.5 30 0.672 0.94
800 127 11 29 0.697

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\sigma_{P}$$, $$MPa$$ $$\epsilon_L$$, % $$\psi$$, % $$KCU\cdot 10^{3}$$, $$\frac{J}{m^2}$$ Treatment
Rod GOST 4543-71 25 1180 1080 12 50 780 Hardening and tempering

Brinell hardness number

Rolling Standard Classifiers Value, HBW
Alloy GOST 4543-71 annealing 269

Technological Properties

Weldability Flake Susceptibility Propensity to temper brittleness
Difficult to weld sensitive not inclined

Critical point temperatures

Ac1, K Ac3(Acm), K Ar3(Arcm), K Ar1, K
740 780 400 300

Analogues

USA Germany
4340 1.6582 (34CrNiMo6)

Standards

Standard Description
GOST 4543-71

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
Cr % Chrome
Cu % Copper
Ni % Nickel
V % Vanadium
P % Phosphorus
C % Carbon
S % Sulfur
Mo % Molybdenum

Description of physical characteristics

Parameter Units of measurement Description
$$E\cdot 10^{9}$$ $$MPa$$ Elastic modulus
$$\alpha\cdot 10^{6}$$ $$K^{-1}$$ Coefficient of thermal (linear) expansion (range 20°C–T)
$$\varkappa$$ $$\frac{W}{m\cdot K}$$ Coefficient of thermal conductivity (the heat capacity of the material)
$$c\cdot 10^{-3}$$ $$\frac{J}{kg\cdot K}$$ The specific heat of the material (range 20°C–T)
$$R\cdot 10^{-6}$$ $$\Omega\cdot m$$ Electrical resistivity

Description of mechanical properties

Parameter Units of measurement Description
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength
$$\sigma_{P}$$ $$MPa$$ Proportionality limit
$$\epsilon_L$$ % Elongation at break (longitudinal)
$$\psi$$ % Reduction in cross section on fracture
$$KCU\cdot 10^{3}$$ $$\frac{J}{m^2}$$ Impact toughness

Designation of types of weldability

Parameter Units of measurement Description
no limits Welding is performed without heating and without subsequent heat treatment
Boundedly welded Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures

Description of temperatures of critical points

Parameter Units of measurement Description
Ac1 K
Ac3(Acm) K
Ar3(Arcm) K
Ar1 K