6HV2S (6H3FS)
Substitute: 6H3FS. Steel is prone to temper embrittlement, does not apply to welded structures. Flock sensitivity: sensitive. Hardness after heat treatment (GOST 5950−2000): HB 10 -1 = 255 MPa .
knives for cold metal cutting, thread rolling dies, punches and crimping dies for cold work dies of complex shape, working with high shock loads.
Classification
| Country |
Section |
Category |
| CIS, Russia, Ukraine |
Tool steel |
Die tool steel |
Chemical composition
| Standard |
Fe, % |
Si, % |
Mn, % |
Cr, % |
Cu, % |
Ni, % |
P, % |
C, % |
S, % |
W, % |
|---|
| GOST 5950-2000 |
93.34–95.6 |
0.5–0.8 |
0.15–0.45 |
1–1.3 |
< 0.3 |
< 0.4 |
< 0.03 |
0.55–0.65 |
< 0.03 |
2.2–2.7 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling |
Standard |
Size, mm |
Tension |
Classifiers |
$$\sigma _{U}$$, $$MPa$$ |
$$\sigma_{P}$$, $$MPa$$ |
$$\epsilon_L$$, % |
$$\psi$$, % |
$$KCU\cdot 10^{3}$$, $$\frac{J}{m^2}$$ |
Treatment |
|---|
| Metal rolling |
|
|
|
|
1770 |
1680 |
7 |
18 |
260 |
Tempering 880 ° C, oil, leave 450 ° C, 2 h |
Brinell hardness number
| Rolling |
Standard |
Classifiers |
Value, HBW |
| Alloy |
GOST 5950-73 |
heat-treated |
255 |
Technological Properties
| Weldability |
Flake Susceptibility |
Propensity to temper brittleness |
|---|
| Not applicable for welded structures |
sensitive |
inclined |
Critical point temperatures
| Ac1, K |
Ac3(Acm), K |
Mn, K |
|---|
| 775 |
810 |
280 |
Analogues
| USA |
Germany |
United Kingdom |
European Union |
Italy |
Spain |
Hungary |
Poland |
Austria |
Czech Republic |
|---|
| T41901 |
1.2550 (60WCrV7) |
BS1 |
55WCrV8 |
55WCrV8KU |
60WCrSi8 |
W6 |
NZ3 |
BOHLERK455 |
19733 |
Standards
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Si |
% |
Silicon |
| Mn |
% |
Manganese |
| Cr |
% |
Chrome |
| Cu |
% |
Copper |
| Ni |
% |
Nickel |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
| W |
% |
Tungsten |
Description of mechanical properties
| Parameter |
Units of measurement |
Description |
| $$\sigma _{U}$$ |
$$MPa$$ |
Ultimate tensile strength |
| $$\sigma_{P}$$ |
$$MPa$$ |
Proportionality limit |
| $$\epsilon_L$$ |
% |
Elongation at break (longitudinal) |
| $$\psi$$ |
% |
Reduction in cross section on fracture |
| $$KCU\cdot 10^{3}$$ |
$$\frac{J}{m^2}$$ |
Impact toughness |
Designation of types of weldability
| Parameter |
Units of measurement |
Description |
| no limits |
|
Welding is performed without heating and without subsequent heat treatment |
| Boundedly welded |
|
Welding is possible with heating up to 100–120 °C and subsequent heat treatment |
| Difficult to weld |
|
For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing |
| Not applicable for welded structures |
|
|
Description of temperatures of critical points
| Parameter |
Units of measurement |
Description |
| Ac1 |
K |
|
| Ac3(Acm) |
K |
|
| Mn |
K |
|