Alloy aluminum AK6M2
Chemical composition
| Al | Aluminum | Rest |
| Fe | Iron | <0.5 |
| Si | Silicon | 5.5 — 6.5 |
| Mg | Magnesium | 0.35 — 0.50 |
| Mn | Manganese | <0.1 |
| Cu | Copper | 1.8 — 2.3 |
| Ni | Nickel | <0.05 |
| Sn | Tin | <0.02 |
| Pb | Lead | <0.02 |
| Ti | Titanium | 0.1 — 0.2 |
| Zn | Zinc | <0.06 |
| Ot | Total impurities | <0.7 |
Casting methods:
Z — sand casting
B — Lost wax casting
K — chill casting
D — injection molding
Mark designation:
h — clean
bees — high purity
och — high purity
l — casting alloys
c — selective
Analogs in Germany
GK-AlSi6Cu4 DIN 1725 Part 2
3.2151.02 DIN 1725 Part 2
G-AlSi6Cu4 DIN 1725 Part 2
3.2151.01 DIN 1725 Part 2
EN AC-45000 DIN EN 1706: 2013
EN AC-45400 DIN EN 1706: 2013
EN AC-AlSi6Cu4 DIN EN 1706: 2013
EN AC-AlSi5Cu3 DIN EN 1706: 2013
EN AC-45000 DIN EN 1706: 2019
EN AC-AlSi6Cu4 DIN EN 1706: 2019
EN AC-45400 DIN EN 1706: 2019
EN AC-AlSi5Cu3 DIN EN 1706: 2019
225 VDS
Analogs in the USA
319.1 AA
319.0 ANSI
EN AC-45000 ASME SB / EN 1706
EN AC-45400 ASME SB / EN 1706
EN AC-AlSi6Cu4 ASME SB / EN 1706
EN AC-AlSi5Cu3 ASME SB / EN 1706
SB 108 (319.0) ASME SB108
SB 108 (A03190) ASME SB108
B 108 (319.0) ASTM B108
B 108 (A03190) ASTM B108
B 179 (319.1) ASTM B179
B 26 (319.0) ASTM B26
B 26 (A03190) ASTM B26
B 275 (A 03190) ASTM B275
B 275 (A 03191) ASTM B275
B 618 (319.0) ASTM B618
B 969 (319.0) ASTM B969
319.0 ASTM B969
319.0 QQ A-596d
J452 (326) SAE J452
A03190 UNS
A03191 UNS
319.0 Included in 2 standards
319.1 Included in 2 standards
A319.1 Included in 2 standards
319.0 Included in 4 standards
For the manufacture of ingots and shaped castings by various casting methods (in sand molds, by investment casting, in chill molds). Technical requirements: GOST 1583−93 Cast aluminum alloys. Technical conditions GOST 1583−93 Cast aluminum alloys. Technical conditions GOST R 55375−12 Primary aluminum and alloys based on it. Stamps
Classification
| Country | Section | Category |
|---|---|---|
| CIS, Russia, Ukraine | Aluminum, aluminum alloys | Foundry aluminum alloys |
Chemical composition
| Standard | Fe, % | Si, % | Mg, % | Mn, % | Ti, % | Cu, % | Zn, % | Ni, % | Al, % |
|---|---|---|---|---|---|---|---|---|---|
| GOST 1583-93 | < 0.6 | 5.5–6.5 | 0.3–0.45 | < 0.1 | 0.1–0.2 | 1.8–2.3 | < 0.06 | < 0.05 | 89.74–92.3 |
Information on suppliers
Mechanical properties at 20 °C
| Rolling | Standard | Size, mm | Tension | Classifiers | $$\sigma _{U}$$, $$MPa$$ | Treatment |
|---|---|---|---|---|---|---|
| Chill casting | GOST 1583-93 | 196–294 |
Analogues
| Germany | USA |
|---|---|
| GK-AlSi6Cu4 | 319.1 |
Standards
| Standard | Description |
|---|---|
| GOST 1583-93 |
Description of chemical elements
| Element | Units of measurement | Description |
|---|---|---|
| Fe | % | Iron |
| Si | % | Silicon |
| Mg | % | Magnesium |
| Mn | % | Manganese |
| Ti | % | Titan |
| Cu | % | Copper |
| Zn | % | Zinc |
| Ni | % | Nickel |
| Al | % | Aluminium |
Description of mechanical properties
| Parameter | Units of measurement | Description |
|---|---|---|
| $$\sigma _{U}$$ | $$MPa$$ | Ultimate tensile strength |