BrA5 (CuAl5)

Details of operating in sea water, parts of chemical engineering; semifinished products (sheet, strip, ribbon, bar, tube, wire)

Classification

Country Section Category
CIS, Russia, Ukraine Bronze Pressureless bronze plated

Chemical composition

Standard Fe, % Si, % Sn, % Mn, % Cu, % Zn, % Al, % Pb, % P, %
GOST 18175-78 < 0.5 < 0.1 < 0.1 < 0.5 92.9–96 < 0.5 4–6 < 0.03 < 0.01

Information on suppliers

Physical characteristics

Temperature, °C $$E\cdot 10^{9}$$, $$MPa$$ $$\alpha\cdot 10^{6}$$, $$K^{-1}$$ $$\varkappa$$, $$\frac{W}{m\cdot K}$$ $$\rho$$, $$\frac{kg}{m^3}$$ $$R\cdot 10^{-6}$$, $$\Omega\cdot m$$
20 120 105 8200 0.1
100 15.6

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers $$\sigma _{U}$$, $$MPa$$ $$\epsilon_L$$, % Treatment
Alloy soft 360–440 60–70
Alloy solid 700–800 4–6

Brinell hardness number

Rolling Standard Classifiers Value, HBW
Alloy soft 550–650
Alloy solid 190–210

Casting and technological parameters

melting point, °C Hot working temperature, °C annealing temperature, °C
1060 750–850 600–700

Coefficients of Friction

coefficient of friction with lubrication coefficient of friction without lubrication
0.007 0.3

Analogues

Germany USA
2.0918 C60600

Standards

Standard Description
GOST 18175-78

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Sn % Tin
Mn % Manganese
Cu % Copper
Zn % Zinc
Al % Aluminium
Pb % Lead
P % Phosphorus

Description of physical characteristics

Parameter Units of measurement Description
$$E\cdot 10^{9}$$ $$MPa$$ Elastic modulus
$$\alpha\cdot 10^{6}$$ $$K^{-1}$$ Coefficient of thermal (linear) expansion (range 20°C–T)
$$\varkappa$$ $$\frac{W}{m\cdot K}$$ Coefficient of thermal conductivity (the heat capacity of the material)
$$\rho$$ $$\frac{kg}{m^3}$$ The density of the material
$$R\cdot 10^{-6}$$ $$\Omega\cdot m$$ Electrical resistivity

Description of mechanical properties

Parameter Units of measurement Description
$$\sigma _{U}$$ $$MPa$$ Ultimate tensile strength
$$\epsilon_L$$ % Elongation at break (longitudinal)

Description of the casting and technological parameters

Parameter Units of measurement Description
melting point °C The temperature at which solid crystalline body makes the transition to the liquid state and Vice versa
Hot working temperature °C The temperature at which the plastic-deformed metal recrystallizes during the pressure treatment
annealing temperature °C The temperature at which the processes return recrystallization and homogenization of the metal to reduce its hardness for subsequent machining