H6VF (9H5F)

Steel does not apply to welded structures. not prone to temper brittleness. Temperature of critical points: Ac1 = 815, Ac3 (Acm) = 845, Ar3 (Arcm) = 775, Ar1 = 625, Mn = 150. Hardness after annealing (GOST 5950−2000): HB 10 -1 = 241 MPa. Substitutes: H12F1, H12M, 9H5 °F.

rezbokatany tools (rolls and dies), hand saw blades, razors, dies, punches, zubonakatniki and other tools for cold deformation, for wood-cutting tools.

Classification

Country Section Category
CIS, Russia, Ukraine Tool steel Die tool steel

Chemical composition

Standard Fe, % Si, % Mn, % Cr, % Cu, % Ni, % V, % P, % C, % S, % W, %
GOST 5950-2000 88.44–91.6 0.1–0.4 0.15–0.45 5.5–6.5 < 0.3 < 0.4 0.5–0.8 < 0.03 1.05–1.15 < 0.03 1.1–1.5

Information on suppliers

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers σU, MPa Treatment
Tape 0.1–4 annealing 880

Brinell hardness number

Rolling Standard Classifiers Value, HBW
Alloy GOST 5950-73 annealing 241

Technological Properties

Weldability Propensity to temper brittleness
Not applicable for welded structures not inclined

Critical point temperatures

Ac1, K Ac3(Acm), K Ar3(Arcm), K Ar1, K Mn, K
815 845 775 625 150

Analogues

USA Germany Japan France United Kingdom Spain
T30102 1.2363 (X100CrMoV5-1) SKD12 Z100CDV5 BA2 X100CrMoV5

Standards

Standard Description
GOST 5950-2000 GOST

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
Cr % Chrome
Cu % Copper
Ni % Nickel
V % Vanadium
P % Phosphorus
C % Carbon
S % Sulfur
W % Tungsten

Description of mechanical properties

Parameter Units of measurement Description
σU MPa Ultimate tensile strength

Designation of types of weldability

Parameter Units of measurement Description
no limits Welding is performed without heating and without subsequent heat treatment
Boundedly welded Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures

Description of temperatures of critical points

Parameter Units of measurement Description
Ac1 K
Ac3(Acm) K
Ar3(Arcm) K
Ar1 K
Mn K