LMtsA57-3-1

Product average strength, high toughness, corrosion resistance

Classification

Country	Section	Category
Country	Section	Category
CIS, Russia, Ukraine	Brass (copper-zinc alloy)	Brass, pressure treated

Chemical composition

Standard	Fe, %	Bi, %	Mn, %	Cu, %	Zn, %	Sb, %	Al, %	Pb, %	P, %
Standard	Fe, %	Bi, %	Mn, %	Cu, %	Zn, %	Sb, %	Al, %	Pb, %	P, %
GOST 15527-2004	< 1	< 0.002	2.5–3.5	55–58.5	35.2–42	< 0.005	0.5–1.5	< 0.2	< 0.01

Information on suppliers

Wish to advertise here?

Physical characteristics

Temperature, °C	$E\cdot 10^{9}$ , $MPa$	$\alpha\cdot 10^{6}$ , $K^{-1}$	$\varkappa$ , $\frac{W}{m\cdot K}$	$\rho$ , $\frac{kg}{m^3}$	$R\cdot 10^{-6}$ , $\Omega\cdot m$
Temperature, °C	$E\cdot 10^{9}$ , $MPa$	$\alpha\cdot 10^{6}$ , $K^{-1}$	$\varkappa$ , $\frac{W}{m\cdot K}$	$\rho$ , $\frac{kg}{m^3}$	$R\cdot 10^{-6}$ , $\Omega\cdot m$
20	104		67	8100	0.121
100		20.1

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\epsilon_L$ , %	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\epsilon_L$ , %	Treatment
Alloy				soft	400–500	40–50
Alloy				solid	700–750	4–8

Brinell hardness number

Rolling	Standard	Classifiers	Value, HBW
Rolling	Standard	Classifiers	Value, HBW
Alloy		soft	850–950
Alloy		solid	1750–1850

Casting and technological parameters

melting point, °C	Hot working temperature, °C	annealing temperature, °C
melting point, °C	Hot working temperature, °C	annealing temperature, °C
870	650–750	600–700

Standards

Standard	Description
Standard	Description
GOST 15527-2004

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Bi	%	Bismuth
Mn	%	Manganese
Cu	%	Copper
Zn	%	Zinc
Sb	%	Antimony
Al	%	Aluminium
Pb	%	Lead
P	%	Phosphorus

Description of physical characteristics

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$E\cdot 10^{9}$	$MPa$	Elastic modulus
$\alpha\cdot 10^{6}$	$K^{-1}$	Coefficient of thermal (linear) expansion (range 20°C–T)
$\varkappa$	$\frac{W}{m\cdot K}$	Coefficient of thermal conductivity (the heat capacity of the material)
$\rho$	$\frac{kg}{m^3}$	The density of the material
$R\cdot 10^{-6}$	$\Omega\cdot m$	Electrical resistivity

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\epsilon_L$	%	Elongation at break (longitudinal)

Description of the casting and technological parameters

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
melting point	°C	The temperature at which solid crystalline body makes the transition to the liquid state and Vice versa
Hot working temperature	°C	The temperature at which the plastic-deformed metal recrystallizes during the pressure treatment
annealing temperature	°C	The temperature at which the processes return recrystallization and homogenization of the metal to reduce its hardness for subsequent machining