MNMts40-1.5 (Constantan)
for the manufacture of semi-finished products (wire, tape and strip), used for electrical purposes and compensating cables
for the manufacture of semi-finished products (wire, tape and strip), used for electrical purposes and compensating cables
Standard | Fe, % | Si, % | Mg, % | Bi, % | Mn, % | Cu, % | Sb, % | Pb, % | As, % | P, % | C, % | S, % | Ni + Co, % |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Standard | Fe, % | Si, % | Mg, % | Bi, % | Mn, % | Cu, % | Sb, % | Pb, % | As, % | P, % | C, % | S, % | Ni + Co, % |
GOST 492-2006 | < 0.5 | < 0.1 | < 0.05 | < 0.002 | 1–2 | 56.1–60 | < 0.002 | < 0.005 | < 0.01 | < 0.005 | < 0.1 | < 0.02 | 39–41 |
Temperature, °C | E\cdot 10^{9}, MPa | \alpha\cdot 10^{6}, K^{-1} | \varkappa, \frac{W}{m\cdot K} | \rho, \frac{kg}{m^3} | R\cdot 10^{-6}, \Omega\cdot m |
---|---|---|---|---|---|
Temperature, °C | E\cdot 10^{9}, MPa | \alpha\cdot 10^{6}, K^{-1} | \varkappa, \frac{W}{m\cdot K} | \rho, \frac{kg}{m^3} | R\cdot 10^{-6}, \Omega\cdot m |
20 | 166 | 21 | 8900 | 0.48 | |
100 | 14.4 |
Rolling | Standard | Size, mm | Tension | Classifiers | \sigma _{U}, MPa | \epsilon_L, % | Treatment |
---|---|---|---|---|---|---|---|
Rolling | Standard | Size, mm | Tension | Classifiers | \sigma _{U}, MPa | \epsilon_L, % | Treatment |
Wire is hard. | GOST 5307 - 77 | 0.02–5 | 640 | ||||
The wire is soft. | GOST 5307 - 77 | 0.1–5 | 440–640 | 15–20 | |||
The tape is hard. | GOST 5189-75 | 640 | |||||
Tape softly. | GOST 5189-75 | 390–590 |
Standard | Description |
---|---|
Standard | Description |
GOST 492-2006 | |
GOST 1790-16 | |
GOST 1791-14 | |
GOST 5189-75 | |
GOST 5307-15 | |
DSTU GOST 492:2007 |
Parameter | Units of measurement | Description |
---|---|---|
Parameter | Units of measurement | Description |
E\cdot 10^{9} | MPa | Elastic modulus |
\alpha\cdot 10^{6} | K^{-1} | Coefficient of thermal (linear) expansion (range 20°C–T) |
\varkappa | \frac{W}{m\cdot K} | Coefficient of thermal conductivity (the heat capacity of the material) |
\rho | \frac{kg}{m^3} | The density of the material |
R\cdot 10^{-6} | \Omega\cdot m | Electrical resistivity |
Parameter | Units of measurement | Description |
---|---|---|
Parameter | Units of measurement | Description |
melting point | °C | The temperature at which solid crystalline body makes the transition to the liquid state and Vice versa |
Hot working temperature | °C | The temperature at which the plastic-deformed metal recrystallizes during the pressure treatment |
annealing temperature | °C | The temperature at which the processes return recrystallization and homogenization of the metal to reduce its hardness for subsequent machining |