NMts2.5
for the manufacture of wire used for the manufacture of candles automotive, aviation and tractor engines
Classification
| Country |
Section |
Category |
| CIS, Russia, Ukraine |
Nickel, nickel alloys |
Nickel alloys |
Chemical composition
| Standard |
Fe, % |
Si, % |
Mg, % |
Bi, % |
Mn, % |
Cu, % |
Sb, % |
Pb, % |
As, % |
P, % |
C, % |
S, % |
Ni + Co, % |
|---|
| GOST 492-2006 |
< 0.4 |
< 0.3 |
< 0.1 |
< 0.002 |
2.3–3.3 |
< 0.2 |
< 0.002 |
< 0.002 |
< 0.03 |
< 0.01 |
< 0.1 |
< 0.015 |
95.2–97.7 |
Information on suppliers
Physical characteristics
| Temperature, °C |
$$E\cdot 10^{9}$$, $$MPa$$ |
$$\alpha\cdot 10^{6}$$, $$K^{-1}$$ |
$$\rho$$, $$\frac{kg}{m^3}$$ |
$$R\cdot 10^{-6}$$, $$\Omega\cdot m$$ |
|---|
| 20 |
210 |
|
8940 |
0.14 |
| 100 |
|
13.4 |
|
|
Mechanical properties at 20 °C
| Rolling |
Standard |
Size, mm |
Tension |
Classifiers |
$$\sigma _{U}$$, $$MPa$$ |
$$\epsilon_L$$, % |
Treatment |
|---|
| Wire |
|
|
|
soft |
640 |
20 |
|
| Wire |
|
|
|
solid |
690 |
|
|
| Alloy |
|
|
|
soft |
450–500 |
|
|
| Alloy |
|
|
|
solid |
900–1000 |
3 |
|
Brinell hardness number
| Rolling |
Standard |
Classifiers |
Value, HBW |
| Alloy |
|
solid |
0–0 |
Casting and technological parameters
| melting point, °C |
Hot working temperature, °C |
annealing temperature, °C |
|---|
| 1440 |
1200–900 |
800–900 |
Standards
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Si |
% |
Silicon |
| Mg |
% |
Magnesium |
| Bi |
% |
Bismuth |
| Mn |
% |
Manganese |
| Cu |
% |
Copper |
| Sb |
% |
Antimony |
| Pb |
% |
Lead |
| As |
% |
Arsenic |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
| Ni + Co |
% |
Nickel + Cobalt |
Description of physical characteristics
| Parameter |
Units of measurement |
Description |
| $$E\cdot 10^{9}$$ |
$$MPa$$ |
Elastic modulus |
| $$\alpha\cdot 10^{6}$$ |
$$K^{-1}$$ |
Coefficient of thermal (linear) expansion (range 20°C–T) |
| $$\rho$$ |
$$\frac{kg}{m^3}$$ |
The density of the material |
| $$R\cdot 10^{-6}$$ |
$$\Omega\cdot m$$ |
Electrical resistivity |
Description of mechanical properties
| Parameter |
Units of measurement |
Description |
| $$\sigma _{U}$$ |
$$MPa$$ |
Ultimate tensile strength |
| $$\epsilon_L$$ |
% |
Elongation at break (longitudinal) |
Description of the casting and technological parameters
| Parameter |
Units of measurement |
Description |
| melting point |
°C |
The temperature at which solid crystalline body makes the transition to the liquid state and Vice versa |
| Hot working temperature |
°C |
The temperature at which the plastic-deformed metal recrystallizes during the pressure treatment |
| annealing temperature |
°C |
The temperature at which the processes return recrystallization and homogenization of the metal to reduce its hardness for subsequent machining |