St6ps

women hammers, spindles, wedges, crowbars and construction etc.

Classification

Country Section Category
CIS, Russia, Ukraine Structural steel Carbonaceous structural steel of ordinary quality

Chemical composition

Standard Fe, % Si, % Mn, % Cr, % Cu, % Ni, % As, % P, % C, % S, % N, %
GOST 380-2005 97.482–99.07 0.05–0.15 0.5–0.8 < 0.3 < 0.3 < 0.3 < 0.08 < 0.04 0.38–0.49 < 0.05 < 0.008

Information on suppliers

Physical characteristics

Temperature, °C \rho, \frac{kg}{m^3}
20 7850

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers \sigma _{U}, MPa \sigma_{P}, MPa \epsilon_L, % Treatment
Hire GOST 535-2005 590 295–315 12–15

Brinell hardness number

Rolling Standard Classifiers Value, HBW
Alloy 197

Technological Properties

Weldability Flake Susceptibility Propensity to temper brittleness
Boundedly welded not sensitive not inclined

Analogues

USA Germany
A572 1.0060 (E335)

Standards

Standard Description
GOST 380-2005

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
Cr % Chrome
Cu % Copper
Ni % Nickel
As % Arsenic
P % Phosphorus
C % Carbon
S % Sulfur
N % Nitrogen

Description of physical characteristics

Parameter Units of measurement Description
\rho \frac{kg}{m^3} The density of the material

Description of mechanical properties

Parameter Units of measurement Description
\sigma _{U} MPa Ultimate tensile strength
\sigma_{P} MPa Proportionality limit
\epsilon_L % Elongation at break (longitudinal)

Designation of types of weldability

Parameter Units of measurement Description
no limits Welding is performed without heating and without subsequent heat treatment
Boundedly welded Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures