Sv-08A

Welding cold drawn wire of low carbon steel welding (surfacing), and the manufacture of electrodes

Classification

Country Section Category
CIS, Russia, Ukraine Materials for welding and soldering Steel welding wire

Chemical composition

Standard Fe, % Si, % Mn, % Cr, % Ni, % Al, % P, % C, % S, % N, %
GOST 2246-70 98.82–99.65 < 0.03 0.35–0.6 < 0.12 < 0.25 < 0.01 < 0.03 < 0.1 < 0.03 < 0.01

Information on suppliers

Properties

Property
Wire rod for the manufacture of welding wire according to TU 14-1-4760-89 Temporary resistance: <420 MPa Relative narrowing:> 60%
Wire according to TU U 322-4-392-96 Diameter: 0.8 mm; Temporary resistance: 780 - 1570 MPa
Diameter: 1.0 - 1.6 mm; Temporary resistance: 780 - 1470 MPa
Diameter: 2mm; Temporary resistance: 780 - 1270 MPa
Diameter:> 2 mm; Temporary resistance: 690 - 1030 MPa
Wire according to TU 14-15-345-94 Diameter: 0.8 mm; Temporary resistance: 780 - 1570 MPa
Diameter: 1.0 - 1.6 mm; Temporary resistance: 780 - 1470 MPa
Diameter: 2mm; Temporary resistance: 780 - 1270 MPa
Wire according to TU 14-1-953-74 Diameter: 2 mm; Temporary resistance: 784 - 1176 MPa
Diameter: 2.5 - 3.0 mm; Temporary resistance: 686 - 1029 MPa
Wire according to TU 14-4-863-77 Thickness: 0.8 - 1.4 mm; Temporary resistance: 880 - 1250 MPa
Thickness: 1.6 mm; Temporary resistance: 880 - 1180 MPa
Thickness: 2 mm; Temporary resistance: 780 - 1080 MPa
According to TU 0934-002-55791017-2010 Diameter: 5.5 - 7.0 mm; Temporary resistance: <420 MPa Relative narrowing:> 55%
Density: 7.86 g / cm3

Analogues

Germany USA
1.0323 (USD7) K01012
1.0351 (RRSD10)

Standards

Standard Description
GOST 2246-70
TU 0934-002-55791017-2010
TU 14-1-4760-89
TU 14-1-953-74
TU 14-108-22-2001
TU 14-15-345-94
TU 14-4-134-73
TU 14-4-863-77
TU У 322-4-392-96
TU 14-4-828-77

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
Cr % Chrome
Ni % Nickel
Al % Aluminium
P % Phosphorus
C % Carbon
S % Sulfur
N % Nitrogen