| Performance data Application temperature: <600 ° C Scaling temperature: 800 ° C |
| Operational characteristics According to GOST R 54803-2011 Nuts Application temperature: -70 - 625 ° C |
| Operational characteristics According to GOST R 54803-2011 Washers Application temperature: -70 - 625 ° C |
| Performance characteristics According to GOST R 54803-2011 Studs Application temperature: -70 - 625 ° C |
| According to GOST 5949 Note. The norms of mechanical properties apply to samples taken from steel with a diameter or thickness of up to 60 mm. |
| For steel with a diameter or thickness of st. 60 to 100mm, a reduction in elongation of 1abs.% Is allowed, |
| relative narrowing by 5abs.% and impact strength by 4.9 J / cm2 at a rate of less than 78.4 J / cm2 and by 9.8 J / cm2 at a rate of 78.4 J / cm2 or more. |
| For steel with a diameter or thickness of st. 100 to 150mm, a reduction in elongation of 3abs.% Is allowed, |
| a relative narrowing of 10 abs.% and impact strength of 9.8 J / cm2 at a rate of less than 78.4 J / cm2 and at 14.7 J / cm2 at a rate of 78.4 J / cm2 or more. |
| Quenching 1140 - 1180 ° С, cooling in water Aging 750 - 800 ° С, holding for 15 h, cooling in air |
| Yield strength:> 295 MPa Tensile strength:> 590 MPa Elongation:> 30% Elongation:> 40% |
| By agreement M1 (tests at elevated temperature) Note By agreement |
| Reference data Note Quenching (normalization) 1150 - 1180 ° С, water cooling Vacation 800 ° С, 15 h, air cooling |
| According to GOST 5949 Temperature: 600 ° C; Long-term tensile strength for 10,000 h:> 235 MPa Long-term tensile strength for 100,000 h:> 216 MPa Creep strength corresponding to 1% of the total deformation per 100,000 h:> 108 MPa |
| According to GOST 5949 Temperature: 650 ° C; Long-term tensile strength for 10,000 h:> 167 MPa Long-term tensile strength for 100,000 h:> 147 MPa Creep strength corresponding to 1% of the total deformation per 100,000 h:> 78 MPa |
| Calculated Properties Density: 7.94 g / cm3 |
| Note Heat-resistant steel Bolts Disks Austenitic steel Rotors |