EI802 (15H12VNMF)

Classification

Country Section Category
CIS, Russia, Ukraine Corrosion-resistant alloys and steels Corrosion-resistant alloys

Chemical composition

Standard Fe, % Si, % Mn, % Cr, % Ti, % Cu, % Ni, % V, % P, % C, % S, % Mo, % W, %
GOST 5632-14 82.065–86.63 < 0.4 0.5–0.9 11–13 < 0.2 < 0.3 0.4–0.8 0.15–0.3 < 0.03 0.12–0.18 < 0.025 0.5–0.7 0.7–1.1

Note: Partial replacement of W by Mo is allowed from the calculation: one mass part of W is replaced by two parts of Mo

Information on suppliers

Properties

Property
Performance data Application temperature: <780 ° C Scaling temperature: 950 ° C
According to GOST 5949 Note. The norms of mechanical properties apply to samples taken from steel with a diameter or thickness of up to 60 mm.
For steel with a diameter or thickness of st. 60 to 100mm, a reduction in elongation of 1abs.% Is allowed,
relative narrowing by 5abs.% and impact strength by 4.9 J / cm2 at a rate of less than 78.4 J / cm2 and by 9.8 J / cm2 at a rate of 78.4 J / cm2 or more.
For steel with a diameter or thickness of st. 100 to 150mm, a reduction in elongation of 3abs.% Is allowed,
a relative narrowing of 10 abs.% and impact strength of 9.8 J / cm2 at a rate of less than 78.4 J / cm2 and at 14.7 J / cm2 at a rate of 78.4 J / cm2 or more.
Annealing 900 - 950 ° С, cooling with a furnace Quenching 1000 - 1020 ° С in oil Tempering 600 - 700 ° С in air
According to GOST 5949 Yield strength:> 590 MPa Tensile strength:> 740 MPa Elongation:> 15%
GOST 5949 Impact strength KCU at 20 ° C:> 59 J / cm2 Relative narrowing:> 45%
According to GOST 5949 Annealing or tempering Hardness HB: <229
According to GOST 5949 As agreed M1 (tests at elevated temperature) Note By agreement
According to GOST 5949 Reference data Note Quenching (normalization) 1000 ° С, oil cooling Vacation 680 ° С, 10 h, air cooling
According to GOST 5949 Temperature: 550 ° C; Long-term tensile strength for 10,000 h:> 235 MPa Long-term tensile strength for 100,000 h:> 196 MPa Creep strength corresponding to 1% of the total deformation per 100,000 h:> 98 MPa
According to GOST 5949 Temperature: 565 ° C; Long-term tensile strength for 10,000 h:> 216 MPa Long-term tensile strength for 100,000 h:> 167 MPa Creep strength corresponding to 1% of the total deformation per 100,000 h:> 88 MPa
According to GOST 5949 Temperature: 580 ° C; Long-term tensile strength for 10,000 h:> 157 MPa Long-term tensile strength for 100,000 h:> 137 MPa Creep strength corresponding to 1% of the total deformation per 100,000 h:> 69 MPa
Calculated Properties Density: 7.88 g / cm3
Note Martensitic Ferritic Steel Heat Resistant Steel

Standards

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
Cr % Chrome
Ti % Titan
Cu % Copper
Ni % Nickel
V % Vanadium
P % Phosphorus
C % Carbon
S % Sulfur
Mo % Molybdenum
W % Tungsten