HN56VMKYU (EP109)
Gas turbine blades and other components to operate under load at temperatures up to 950 ° C.
Classification
| Country |
Section |
Category |
| CIS, Russia, Ukraine |
Heat resistant steels and alloys |
Heat resistant alloys |
Chemical composition
| Standard |
Fe, % |
Si, % |
B, % |
Mn, % |
Co, % |
Cr, % |
Ni, % |
Al, % |
Ce, % |
P, % |
C, % |
S, % |
Mo, % |
W, % |
|---|
| GOST 5632-72 |
< 1.5 |
< 0.6 |
< 0.02 |
< 0.3 |
11–13 |
8.5–10.5 |
52.234–62.6 |
5.4–6.2 |
< 0.02 |
< 0.015 |
< 0.1 |
< 0.011 |
6.5–8 |
6–7.5 |
Information on suppliers
Physical characteristics
| Temperature, °C |
$$E\cdot 10^{9}$$, $$MPa$$ |
$$\alpha\cdot 10^{6}$$, $$K^{-1}$$ |
$$\varkappa$$, $$\frac{W}{m\cdot K}$$ |
$$\rho$$, $$\frac{kg}{m^3}$$ |
|---|
| 20 |
210 |
|
|
8450 |
| 100 |
|
11.8 |
8.8 |
|
| 200 |
|
12.2 |
10.5 |
|
| 300 |
|
12.7 |
11.8 |
|
| 400 |
|
13.1 |
13.8 |
|
| 500 |
188 |
13.4 |
15.9 |
|
| 600 |
183 |
13.6 |
18.4 |
|
| 700 |
176 |
14.1 |
20.9 |
|
| 800 |
169 |
14.8 |
23.4 |
|
| 900 |
|
15.7 |
25.9 |
|
| 1000 |
|
17 |
|
|
Mechanical properties at 20 °C
| Rolling |
Standard |
Size, mm |
Tension |
Classifiers |
$$\sigma _{U}$$, $$MPa$$ |
$$\sigma_{P}$$, $$MPa$$ |
$$\epsilon_L$$, % |
$$\psi$$, % |
$$KCU\cdot 10^{3}$$, $$\frac{J}{m^2}$$ |
Treatment |
|---|
| Rod |
GOST 23705 - 79 |
|
|
|
1080–1280 |
750 |
9–15 |
11–16 |
196–490 |
Heat 1220 ° C, 4-6 hours, air cooling, Aging 950 ° C, 8 hours, air cooling |
Brinell hardness number
| Rolling |
Standard |
Classifiers |
Value, HBW |
| Rod |
GOST 23705 - 79 |
Hardening, aging |
302–363 |
Standards
Description of chemical elements
| Element |
Units of measurement |
Description |
| Fe |
% |
Iron |
| Si |
% |
Silicon |
| B |
% |
Bor |
| Mn |
% |
Manganese |
| Co |
% |
Cobalt |
| Cr |
% |
Chrome |
| Ni |
% |
Nickel |
| Al |
% |
Aluminium |
| Ce |
% |
Cerium |
| P |
% |
Phosphorus |
| C |
% |
Carbon |
| S |
% |
Sulfur |
| Mo |
% |
Molybdenum |
| W |
% |
Tungsten |
Description of physical characteristics
| Parameter |
Units of measurement |
Description |
| $$E\cdot 10^{9}$$ |
$$MPa$$ |
Elastic modulus |
| $$\alpha\cdot 10^{6}$$ |
$$K^{-1}$$ |
Coefficient of thermal (linear) expansion (range 20°C–T) |
| $$\varkappa$$ |
$$\frac{W}{m\cdot K}$$ |
Coefficient of thermal conductivity (the heat capacity of the material) |
| $$\rho$$ |
$$\frac{kg}{m^3}$$ |
The density of the material |
Description of mechanical properties
| Parameter |
Units of measurement |
Description |
| $$\sigma _{U}$$ |
$$MPa$$ |
Ultimate tensile strength |
| $$\sigma_{P}$$ |
$$MPa$$ |
Proportionality limit |
| $$\epsilon_L$$ |
% |
Elongation at break (longitudinal) |
| $$\psi$$ |
% |
Reduction in cross section on fracture |
| $$KCU\cdot 10^{3}$$ |
$$\frac{J}{m^2}$$ |
Impact toughness |