HN80TBYU (EI607A, 8-41)

Turbine blades, fasteners…

blades, fasteners turbines, long operating at temperatures up to 700 ° C.

Classification

Country	Section	Category
Country	Section	Category
CIS, Russia, Ukraine	Heat resistant steels and alloys	Heat resistant alloys

Chemical composition

Standard	Fe, %	Si, %	Mn, %	Cr, %	Ti, %	Ni, %	Al, %	P, %	C, %	S, %	Nb, %
Standard	Fe, %	Si, %	Mn, %	Cr, %	Ti, %	Ni, %	Al, %	P, %	C, %	S, %	Nb, %
GOST 5632-72	< 3	< 0.8	< 1	15–18	1.8–2.3	72.293–81.7	0.5–1	< 0.015	< 0.08	< 0.012	1–1.5

Information on suppliers

Wish to advertise here?

Physical characteristics

Temperature, °C	$E\cdot 10^{9}$ , $MPa$	$\alpha\cdot 10^{6}$ , $K^{-1}$	$\varkappa$ , $\frac{W}{m\cdot K}$	$\rho$ , $\frac{kg}{m^3}$	$R\cdot 10^{-6}$ , $\Omega\cdot m$
Temperature, °C	$E\cdot 10^{9}$ , $MPa$	$\alpha\cdot 10^{6}$ , $K^{-1}$	$\varkappa$ , $\frac{W}{m\cdot K}$	$\rho$ , $\frac{kg}{m^3}$	$R\cdot 10^{-6}$ , $\Omega\cdot m$
20	224			8300
100	221		13.4		1.17
200	215		15.5		1.18
300	210	13.1	17.9		1.19
400	204	14	20.1		1.2
500	197	14.4	24.3		1.22
600	188	14.9	26.3		1.23
700	178	15.6	26.3		1.24
800	168	16.35	28.9

Mechanical properties at 20 °C

Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{P}$ , $MPa$	$\epsilon_L$ , %	$\psi$ , %	$KCU\cdot 10^{3}$ , $\frac{J}{m^2}$	Treatment
Rolling	Standard	Size, mm	Tension	Classifiers	$\sigma _{U}$ , $MPa$	$\sigma_{P}$ , $MPa$	$\epsilon_L$ , %	$\psi$ , %	$KCU\cdot 10^{3}$ , $\frac{J}{m^2}$	Treatment
Rod					950	650	18	22	700

Technological Properties

Weldability
Weldability
Difficult to weld

Analogues

USA
USA
UNS07750

Standards

Standard	Description
Standard	Description
GOST 5632-72
TU 14-1-1358-74
GOST 5632-14

Description of chemical elements

Element	Units of measurement	Description
Element	Units of measurement	Description
Fe	%	Iron
Si	%	Silicon
Mn	%	Manganese
Cr	%	Chrome
Ti	%	Titan
Ni	%	Nickel
Al	%	Aluminium
P	%	Phosphorus
C	%	Carbon
S	%	Sulfur
Nb	%	Niobium

Description of physical characteristics

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$E\cdot 10^{9}$	$MPa$	Elastic modulus
$\alpha\cdot 10^{6}$	$K^{-1}$	Coefficient of thermal (linear) expansion (range 20°C–T)
$\varkappa$	$\frac{W}{m\cdot K}$	Coefficient of thermal conductivity (the heat capacity of the material)
$\rho$	$\frac{kg}{m^3}$	The density of the material
$R\cdot 10^{-6}$	$\Omega\cdot m$	Electrical resistivity

Description of mechanical properties

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
$\sigma _{U}$	$MPa$	Ultimate tensile strength
$\sigma_{P}$	$MPa$	Proportionality limit
$\epsilon_L$	%	Elongation at break (longitudinal)
$\psi$	%	Reduction in cross section on fracture
$KCU\cdot 10^{3}$	$\frac{J}{m^2}$	Impact toughness

Designation of types of weldability

Parameter	Units of measurement	Description
Parameter	Units of measurement	Description
no limits		Welding is performed without heating and without subsequent heat treatment
Boundedly welded		Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld		For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures