HN75MBTYU (EI602)

Details of gas pipeline systems, equipment.

details of pipeline systems, hardware, parts of the combustion chambers with a limited service life at temperatures up to 950 degrees C; heat-resisting alloy

Classification

Country Section Category
CIS, Russia, Ukraine Heat resistant steels and alloys Heat resistant alloys

Chemical composition

Standard Fe, % Si, % Mn, % Cr, % Ti, % Ni, % Al, % P, % C, % S, % Nb, % Mo, %
GOST 5632-72 < 3 < 0.8 < 0.4 19–22 0.35–0.75 68.568–77.6 0.35–0.75 < 0.02 < 0.1 < 0.012 0.9–1.3 1.8–2.3

Information on suppliers

Physical characteristics

Temperature, °C E\cdot 10^{9}, MPa \alpha\cdot 10^{6}, K^{-1} \varkappa, \frac{W}{m\cdot K} \rho, \frac{kg}{m^3}
20 190 8300
100 12.4 13.45
200 13.4 15.3
300 14.2 16.7
400 165 15 18.5
500 163 15.8 20.2
600 150 16.5 22.3
700 137 18.1 24.4

Mechanical properties at 20 °C

Rolling Standard Size, mm Tension Classifiers \sigma _{U}, MPa \sigma_{P}, MPa \epsilon_L, % \psi, % Treatment
Sheet GOST 24982-81 900–930 40 Hardening of 1050-1080 ° C
Castings GOST 7769-82 860 400 43 37 Hardening of 1050-1080 ° C, air

Technological Properties

Weldability
no limits

Standards

Description of chemical elements

Element Units of measurement Description
Fe % Iron
Si % Silicon
Mn % Manganese
Cr % Chrome
Ti % Titan
Ni % Nickel
Al % Aluminium
P % Phosphorus
C % Carbon
S % Sulfur
Nb % Niobium
Mo % Molybdenum

Description of physical characteristics

Parameter Units of measurement Description
E\cdot 10^{9} MPa Elastic modulus
\alpha\cdot 10^{6} K^{-1} Coefficient of thermal (linear) expansion (range 20°C–T)
\varkappa \frac{W}{m\cdot K} Coefficient of thermal conductivity (the heat capacity of the material)
\rho \frac{kg}{m^3} The density of the material

Description of mechanical properties

Parameter Units of measurement Description
\sigma _{U} MPa Ultimate tensile strength
\sigma_{P} MPa Proportionality limit
\epsilon_L % Elongation at break (longitudinal)
\psi % Reduction in cross section on fracture

Designation of types of weldability

Parameter Units of measurement Description
no limits Welding is performed without heating and without subsequent heat treatment
Boundedly welded Welding is possible with heating up to 100–120 °C and subsequent heat treatment
Difficult to weld For obtaining quality welded joints, additional operations are required: heating up to 200–300 °C for welding, heat treatment after welding — annealing
Not applicable for welded structures